目前國造槍枝槍管材料大部份為鉻鉬釩合金鋼，且使用冷鍛機鍛造，頻繁的實彈測試任務，伴隨的就是槍管處於高溫狀態，故本研究使用槍管料（鉻鉬釩合金圓鋼），試片製作後除原常溫外，分於加熱爐加熱至100℃、200℃、400℃、600℃，持溫20分鐘並使用空氣冷卻。最後再針對前述試片進行顯微組織觀察、維氏硬度試驗及電化學腐蝕機制量測，以了解射擊時槍管於各溫度之變化。
由本實驗得知鉻鉬釩合金鋼於常溫至400℃時，顯微組織原則上不會有太大變化，且組織分佈均勻，惟加熱至600℃時型態會有所改變，肥粒鐵組織變大許多，對照600℃硬度值明顯變低，HV值僅剩129；此外，由電化學極化曲線之腐蝕電流量測結果得知，槍管料於400℃腐蝕最快，其次為常溫，而後為溫度200℃、溫度100℃。

At present, most of the gun barrel materials made in Taiwan are chromium-molybdenum-vanadium alloy steel, which is forged by cold forging machines.Frequent live ammunition testing tasks are accompanied by the high temperature of the barrel,
Therefore, this research focus on the property of barrel material (chromium-molybdenum-vanadium alloy round steel) with various temperatures in heat treatment furnace. The specimens is exposed to 100℃, 200℃, 400℃ and 600℃ for 20 minutes, then cooled by air.
The specimens are carried out to microstructure observation, Vickers hardness test, and electrochemical corrosion mechanism measurement. To understand the changes of the barrel at various temperatures. From this experiment, it is known that the metallograph of chromium- molybdenum- vanadium alloy steel at 400℃ will not change much, and the structure is uniform.
However, the α-Fe structure of the 600℃ specimen will become much larger; and the HV value of 600℃ specimen is only 129.
In addition, from the results of the electrochemical test, it is known that the specimen corrodes fastest at 400°C, followed by ambient temperature, and then at 200°C and 100°C.

中文摘要 ii
英文摘要 iii
誌謝 iv
表目錄 vii
圖目錄 viii
第一章 緒論 1
1.1 研究動機 1
1.2 研究背景 3
1.3 研究目的 9
1.4 論文架構 11
第二章 基礎理論 12
2.1 槍管簡介 12
2.2 槍管材料簡介 14
2.3 槍管加工介紹 16
2.4 鍛造介紹 18
2.5 金相實驗 21
2.6 槍枝測試介紹 24
2.7 電化學量測 25
第三章 實驗設備與方法 28
3.1 實驗流程圖 28
3.2 試驗試片製備 30
3.3 金相觀察 33
3.4 硬度量測 36
3.5 電化學：極化曲線腐蝕量測 37
第四章 結果與討論 39
4.1 金相觀察結果 39
4.2 硬度試驗 45
4.3 電化學：極化曲線腐蝕量測結果 47
第五章 結論與未來展望 62
5.1 結論 62
5.2 未來展望 64
參考文獻 65

[1]Engel, E. & Eckstein, R.,2002, “Microforming-from basic research to its realization”, Journal of Materials Processing Technology, vol. 125-126, pp.35-44.
[2]Egerer, E. & Engel, U., 2004, “Process characterization and material flow in microforming at elevated temperatures”, Journal of Manufacturing Processes, vol. 6, No.1, pp.1-6.
[3]Eichenhueller, B. & Engel, E., 2007, “microforming at elevated temperature- formig and material behaviour”, The International Journal of Advanced Manufacturing Technology, vol.33 ,pp.119-124.
[4]林劍塵，2010，溫度與晶粒尺寸對純銅前後向微擠製之影響，國立高雄應用科技大學，碩士論文。
[5]黃俊傑，2020，構造用鎳鉻鉬合金鋼JIS SNCM439沃斯回火熱處理之研究，國立高雄科技大學，碩士論文。
[6]柯豐富，2015，差溫加熱微鍛造成形之研究，國立高雄應用科技大學，碩士論文。
[7]Wang, J. H., Wei, F. I. & Chang, Y. S.,1997, “The corrosion mechanisms of carbon steel and weathering steel in SO_2 polluted atmospheres”, Mater. Chem. Phys., 47: 1.
[8]Medvedeva, M. L. & Guryanov, V. V. , 2002, “On the corrosion state of plants for purifying natural gas from acid components”, [J]. Prot. Met. 38(3): 284-288.
[9]Zhang, X., Yang, M., Wang, X., Lin, A. & Gan, F., 2010, “CORROSION BEHAVIOR OF MILD STEEL UNDER CONDITION OF H2S SOLUTION”, Journal of Chinese Society for Corrosion and Protection, pp.465-468, Vol.30 , No.6.
[10]Chao, Y., Zhou, Y., Di, Q., Wang, L. & Cheng, S., 2014, “Effect of Micro-alloying Elements on Corrosion Resistance of Low Carbon Steels”, Journal of Chinese Society for Corrosion and Protection, pp.70-74, Vol.34, No.1.
[11]林俊穎，2020，應用超冷處理提升410不銹鋼狙擊槍管精度之研究，正修科技大學，碩士論文。
[12]馬慶恆，崔中旺，2004，陀螺原理與螺旋膛線，科技文萃，8期。
[13]NEWS ZH中文網，軍事，現代槍械槍管：現代槍械槍管一般采用什麽材料以及使用壽命。
[14]https://www.zhdate.com/tw/news_military/48616.html
[15]李榮顯，1986，塑性加工學，三民書局。
[16]黃永昌，2019， T型螺栓冷鍛頭部成形設計改善，高雄科技大學，碩士論文。
[17]薛福男，1991，塑性加工學，全華科技圖書股份有限公司。
[18]吳家豪，2006， Al_xFeCoNiCrMo_0.5高熵合金之腐蝕及電化學性質，國立清華大學，碩士論文。
[19]Tait, W. S., 1994, An introduction to electrochemical corrosion testing for practicing engineers and scientists, Chapter 6, Racine, Wisconsin.
[20]林英凱，2019，特殊熔射工業管線耐蝕性之研究，國立高雄科技大學，博士論文。
[21]劉福雄，1999，防蝕技術，全華科技圖書公司。
[22]Jones, D. A. , 1996, Principles and prevention of corrosion Ch3, Electrochenmical kinentics of corrosion, pp. 75-100.