本研究利用向列型液晶摻雜十二氫氧基硬酯酸(12-hydroxysteric acid，以下簡稱HSA)製成樣本，並觀察其特性。之前的研究發現HSA 摻雜向列型液晶而且在玻璃基板沒有經過任何配向處理的情況下，HSA對液晶擁有自發性垂直排列特性的現象，這免除一般垂直配向對基板做表面處理的過程，並簡化製程。我們發現HSA引致垂直配向特性會與液晶灌入空樣本的溫度及灌入後靜置的時間有關。根據這幾點，我們製作了不同靜置時間和不同灌入溫度的摻雜HSA之液晶樣本，利用HSA 自發性垂直排列的特性，讓液晶擁有形成不同的預傾角，並查看它引致垂直配向的強度。

In this study, a 12-hydroxystearic acid (HSA) doped nematic liquid crystal (LC) cell was fabricated. The spontaneous vertical alignment of LC molecules on ITO glasses by doping HSA into LCs was examined. This characteristic is very convenient due to the simple fabrication process. Multistable characteristic by doping HSA into LCs was examined. Various sample temperatures and fabrication times at a high temperature were tested in the experiments. The results demonstrated that the pretilt angle of the LC molecules can be controlled by sample temperature and fabrication time at a high temperature.

中文摘要 ……………………………………..……………………….. ……………………….ⅰ
英文摘要 ………………………………………….……….………………………………...ⅱ
誌謝 …………………………………………………………………………….……....ⅲ
目錄 ………………………………………………………..………………………........ⅳ
表目錄 ..……………………………………………………………..…………………….ⅵ
圖目錄 ..……………………………………………………………….. ……………………..ⅶ
符號說明 …………………………………………………………………………………....ⅸ
第一章 緒論 ………………………………………………………………………..1
第二章 液晶簡介 ……………………………………………………………………2
2.1 何謂液晶 ……………………………………………………………………2
2.1.1 液晶的定義 ..………………………………………………………………..3
2.1.2 液晶的分類 ..………………………………………………………………..3
2.2 液晶物理 ……………………………………………………………………8
2.2.1 液晶的雙折射性 ……………………………………………………………8
2.2.2 液晶的介電異向性 ………………………………………………………..10
2.2.3 溫度對液晶的影響 ………………………………………………………..11
2.2.4 液晶的連續彈性理論 ……………………………………………………..12
2.2.5 Freedericksz Transition …………………………………..........................13
第三章 實驗理論 …………………………………………………………………..14
3.1 自組織材料引致液晶分子垂直排列………………………………………14
3.2 自組織材料穩固液晶分子排列……………………………………………14
3.2 液晶的相位延遲 …………………………………………………………..16
3.3 溝槽理論 …………………………………………………..........................17
第四章 材料介紹與實驗架構 …….….……………………………………………18
4.1 材料介紹 …………………………………………………………………..18
4.1.1 向列型液晶 ………………………………………………………………..18
4.1.2 十二氫氧基酯酸 …………………………………………………………..18
4.2 樣本製作 …………………………………………………………………..20
4.2.1 材料配置 …………………………………………………………………..20
4.2.2 無配向製作 ………………………………………………………………..20
4.2.3 水平配向製作 ……………………………………………………………..20
4.2.4 製作液晶盒 ………………………………………………………………..20
4.3 實驗架構 …………………………………………………………………..21
4.3.1 液晶層厚度量測 …………………………………………………………..21
4.3.2 穿透度-電壓曲線(T-V curve)量測 ………………………..........................22
4.3.3 相位量測……………………………………………………………………23
4.3.4 預傾角量測…………………………………………………………………24
第五章 結果與討論 ………………………………………………………………..25
5.1 正型液晶LC200摻雜HSA………………………………………………..25
5.1.1 HSA摻雜正型液晶LC200引致垂直配向特性…………………………..25
5.1.2 HSA摻雜正型液晶LC200的多穩態特性………………………………..25
5.2 改變0.8wt%HSA+LC200灌入後所靜置的時間來調控預傾角…………..26
5.3 改變0.8wt%HSA+LC200灌入的溫度來調控預傾角……………………..28
5.4 改變PVA製程溫度和液晶灌入的溫度來調控預傾………………………30
第六章 結論與未來工作 …………………………………………………………..34
6.1 結論 ………………………………………………………………………..34
6.2 未來工作 …………………………………………………………………..34
參考文獻 ………………………………………………………………………………35

[1] J. Y. L. Ho, V. G. Chigrinov, and H. S. Kwok, “Variable liquid crystal pretilt angles generated by photoalignment of a mixed polyimide alignment layer”, Appl. Phys. Lett. 90, 243506 (2007).
[2] H. D. Jayathilake, M. H. Zhu, C. Rosenblatt, A. N. Bordenyuk, C. Weeraman, and A. V. Benderskii, “Rubbing-induced anisotropy of long alkyl side chains at polyimide surfaces”, J. Chem. Phys. 125, 064706 (2006).
[3] T. J. Chen and K. L. Chu, “Pretilt angle control for single-cell-gap transflective liquid crystal cells”, Appl. Phys. Lett. 92, 091102 (2008).
[4] J. B. Kim, K. C. Kim, H. J. Ahn, B. H. Hwang, J. T. Kim, S. J. Jo, C. S. Kim, H. K. Baik, C.J. Choi, M. K. Jo, Y. S. Kim, J. S. Park, and D. Kang, “No bias pi cell using a dual alignment layer with an intermediate pretilt angle”, Appl. Phys. Lett. 91, 023507 (2007).
[5] 王智弘，2014，”十二氫氧基硬酯酸摻雜於液晶引致垂直排列之研究”， 國立虎尾科技大學光電工程系光電與材料科技碩士班碩士論文。
[6] 柯俐妘，2017，”十二氫氧基硬酯酸摻雜於液晶引致垂直排列之研究”，國立虎尾科技大學光電工程系光電與材料科技碩士班碩士論文。.
[7] 黃三宜，2006，“聚合物表面引致況素吸附達成液晶光柵開關”，國力成功大學物理研究所碩士論文。
[8] 鄭和宜，2010，“以光導電薄膜之液晶元件探討光偏振現象”，國立中山大學物理學系研究所碩士論文。
[9] P. Yeh, C. Gu, 1999, Optics of Liquid Crystal Displays, A Wiley Interscience Publication, New York.
[10]李美儒，2004，“摻雜偶氮染料之向列相液晶薄膜在雙光子光柵下引致的光折變效 應”，國立成功大學物理研究所碩士論文。
[11] H. C. Lin, C. H. Wang, J. K. Wang and S. F. Tsai, “Fast response and spontaneous alignment in liquid crystals doped with 12-hydroxystearic acid gelators”, Materials, 11, 745(2018)
[12] N. Mizoshita, K. Hanabusa, T. Kato, “Fast and high-contrast electro-optical switching of liquid-crystalline physical gels: formation of oriented mircophase-separated structures”, Adv. Funct. Mater., 13, 313, April(2003).
[13] N. Mizoshita, Y. Suzuki, K. Hanabusa, T. Kato, “Bistable nematic liquid crystals with self-assembled fibers”, Adv. Funct. Mater., 17, 692, March(2005).
[14] A. Y. G. Fuh, J. T. Chiang, Y. S. Chien, C. J. Chang, and H. C. Lin, 2012, “Multustable phase-retardation plate based on gelator-doped liquid crystals”, Appl. Phys. Express, 5, 7, 072503, July(2012).
[15] D. W. Berreman, “Solid surface shape and the alignment of an adjacent nematic liquid crystal”, Phys. Rev. Lett, 28, 1683, June(1972).
[16] S. Shalel-Levanon, A. Marmur, “Validity and accuracy in evaluating surface tension of solids by additive approaches”, J. Colloid Interf. Sci., 262(2), 489-499 (2003).
[17] J. S. Gwag, “Simple method for measuring the high pretilt angle of nematic liquid crystals” J. Appl. Phys. 93, 4936 (2003)
[18] D. K. Owens, R.C. Wendt, “Estimation of the surface energy of polymer”, J. Appl. Poly. Sci., 13, 1741-1747 (1969).