本論文主要研究奈米二氧化矽的添加對PVB/玻璃陶瓷分別在氮氣與空氣下、不同添加比例、以及不同操作條件的熱解動力分析。以熱重分析儀（Thermo-gravimetric analysis，TGA）觀察複合材料的熱重損失曲線，並以傅立葉紅外線光譜儀（Fourier Transform Infrared Spectroscopy）分析其熱解氣體的光譜變化。再者，利用Arrhenius關係式所推導的動力方程式解析解，導出以非線性加熱方式進行實驗，同時依據等轉化率的原則，分析樣品的熱解動力現象。實驗結果發現奈米二氧化矽的添加對PVB/玻璃陶瓷在氮氣與空氣下的熱解都有影響。且奈米二氧化矽/PVB/玻璃陶瓷在氮氣與空氣下都是屬於多重反應現象，熱解動力參數可由本論文所提出之分析方法求得，由動力三參數反映出裂解機構的複雜性。

Kinetic analysis of thermal degradation of poly(vinyl butyral)(PVB)/glass ceramic with nano-silica was investigated in different atmosphere, composition, and operating conditions. Kinetic triplets and reaction pathways of the composite sample were analyzed by thermogravimetry (TG) and Fourier-Transform Infrared spectroscopy (FT-IR) measurements using the proposed algorithm. Results of the kinetic analysis revealed that the thermal degradation mechanism of the composites is multiple reaction steps. In nitrogen atmosphere, the degradation temperature of the composites is higher because of the presence of nano-silica. In air atmosphere, the effects of nano-silica on PVB/ glass ceramic thermal degradation were verified by detecting the volatile gas.

中文摘要…………………………………………………………………Ⅰ
英文摘要…………………………………………………………………Ⅱ
目錄……………………………………………………………………....Ⅲ
表目錄……………………………………………………………………Ⅴ
圖目錄……………………………………………………………………Ⅶ
第一章 緒論…………………………………………………………...1
1.1 簡介…………………………………………………………………..1
1.2 研究動機與目的……………………………………………………..2
第二章 文獻回顧……………………………………………………...4 2.1 低溫共燒陶瓷製程與技術…………………………………………..4
2.2 高分子熱解動力分析………………………………………………..6
2.3 高分子裂解……………………………..……………….…………...9
2.4 奈米陶瓷材料……………………………………………………….15
第三章 熱解動力分析方法導衍……………………………………17
第四章 實驗方法..............................................................................22
4.1 實驗設計與流程......................................................................................22
4.2 藥品、設備與材料材料製備…………………………………...…..24
4.3 熱重分析實驗與動力計算……………………………………….....28
4.4傅立葉轉換紅外線光譜分析實驗與動力計算……………………..33
第五章 結果與討論………………………………………………...…35
5.1 碳酸鈣的熱解 ..…..35
5.2 PVB/玻璃陶瓷粉體複合材料的熱解分析…………………………57
5.3 PVB/奈米二氧化矽/玻璃陶瓷複合材料的熱解分析……….……..70
第六章 結論……………………………………………………………89
第七章 文獻回顧………………………………………………………90
附錄………………………………………………………………………92

A.K. Galwey, M.E. Brown, Thermochim. Acta 386 (2002) 91-98
A. K. Burnham, Thermochimica Acta 355 (2000) 165-170
A.W. Coats, J.P. Redfern, Nature 201 (1964) 68-71.
B. Roduit, Thermochimica Acta 355 (2000) 171-180
Burnhame, J. Opfermannf, R. Streyg, H.L. Andersong, A. Kemmlerg, R. Keuleersh, J. Janssensh, H.O. Desseynh, Chao-Rui Lii, Tong B. Tangi, B. Roduitj, J. Malekk, T. Mitsuhashi, Thermochim. Acta 355 (2000) 125-143.
C.D. Doyle, J. Appl. Polym. Sci. 6 (1962) 639-642.
E. Segal, C. Popescu, Thermochimica Acta 48 (1981) 383-385
J. Simon, E. Debreczeny, J. of Thermal Analysis, 3 (1971) 301-305
J. Zsako, J. of Thermal Analysis, 2 (1970) 459-460
J. A. Lewis, Annu. Rev. Mater. Sci. 27 (1997) 147—73
K. Feng, S.J. Lombardo, J. Am. Ceram. Soc. 86 (2003) 234-240.
L. C. K. Liau, J. Y. Liau, Y. T. Chen, J. of Applied Polymer Science 93 (2004) 2142—2149
L. C. K. Liau, J. Y. Liau, Ind. Eng. Chem. Res. 43 (2004) 1938-1943
L. C. K. Liau, T. C. K. Yang, D. S. Viswanath, Polymer Engeering and Science 36 (1996) no.21 2589-2600
L. C. K. Liau, D. S. Viswanath, Ind. Eng. Chem. Res. 37 (1998) 49-57
L. C. K. Liau, J. Y. Liau, Y. T. Chen, J. of Applied Polymer Science 93 (2004) 2142—2149
M. Maciejewski, Thermochimica Acta 355 (2000) 145-154
M. E. Brown and A. K. Galway, Therochim. Acta 387 (2002) 173-183.
M.E. Browna,, M. Maciejewskib, S. Vyazovkinc, R. Nomend, J. Sempered, A. Burnhame, J. Opfermannf, R. Streyg, H.L. Andersong, A. Kemmlerg, R. Keuleersh, J. Janssensh, H.O. Desseynh, Chao-Rui Lii, Tong B. Tangi, B. Roduitj, J. Malekk, T. Mitsuhashi, Thermochim. Acta 355 (2000) 125-143.
S. Vyazovkin, Thermochimica Acta 355 (2000) 155-163
S. Vyazovkin, J. Comp. Chem. 18 (1997) 393-402.
T. V. Lee, S. R. Beck, AIChE Journal 30 (1984) 517-519
V. Marcu, E. Segal, Thermochimica Acta 24 (1978) 178-181
張立德,奈米材料與奈米結構,滄海書局,台中市,2002
林鴻欽,中華民國陶業研究學會會刊,21,4,(2002)